IPC分类号：
B44C1/17 | B44C3/02 | B44C5/04 | B29C45/14 | B32B27/06 | B32B27/40
国民经济行业分类号：
C2438 | C2436 | C2435 | C2434 | C2433 | C2432 | C2431 | C3076 | C3075 | C2439
当前申请(专利权)人：
LEONHARD KURZ STIFTUNG & CO. KG
原始申请(专利权)人：
LEONHARD KURZ STIFTUNG & CO. KG
发明人：
FALGNER, STEFFEN | SUSS, CHRISTOPH | OBERNDÖRFER, SVEN
摘要：
Methods for producing a transfer film (1), in particular IMD transfer film (1), wherein the following steps are carried out, in particular in the specified order:preparing a carrier ply (3),preparing a transfer ply (2) having a decorative ply (21), wherein the transfer ply (2) has been or is arranged on the carrier ply (3),applying one or more forming elements (40) to the carrier ply (3), wherein the one or more forming elements (40) have a three-dimensional shape and are applied register-accurately with respect to the decorative ply (21).
A method for coating a plastic injection-molded article with the transfer film, as well as the transfer film and the plastic injection-molded article.
技术问题语段：
The technical problem addressed in this patent is to improve the production of transfer films and plastic injection-molded articles with improved decorative and functional properties, by introducing a method for producing a transfer film with a three-dimensional shape that is accurately registered with respect to a decorative ply and by using a forming element that has a three-dimensional shape and is applied register-accurately with respect to the decorative ply. This allows for better transfer of the transfer film onto the plastic injection-molded article during the production process.
技术功效语段：
The present invention relates to a method for producing a transfer film and a plastic injection-molded article with improved decorative and functional properties. The method involves preparing a carrier ply and a transfer ply with a decorative ply, applying one or more forming elements to the carrier ply in a way that ensures accurate registration with the decorative ply, and then back-injection molding the transfer film with an injection-molding compound. The resulting plastic injection-molded article comprises an injection-molding compound and a transfer film with a decorative ply and a molding of a three-dimensional shape that is introduced register-accurately with respect to the decorative ply. The technical effects of this invention include improved properties of the transfer film and the plastic injection-molded article, such as improved decorative and functional properties.
权利要求：
1. A method for producing a transfer film, wherein the following steps are carried out:
a) preparing a carrier ply,
b) preparing a transfer ply comprising a decorative ply, wherein the transfer ply has been or is arranged on the carrier ply,
c) applying one or more forming elements to the carrier ply, wherein the one or more forming elements have a three-dimensional shape and are applied register-accurately with respect to the decorative ply.
2. The method according to claim 1, wherein
the transfer ply has been or is applied to a first side of the carrier ply and the one or more forming elements are applied to a second side of the carrier ply lying opposite the first side.
3. (canceled)
4. (canceled)
5. The method according to claim 1, wherein,
in step c) one or more first layers of the one or more forming elements are applied using a digital printing method.
6. The method according to claim 1, wherein
a layer of the one or more forming elements applied last in step c) is applied using a digital printing method.
7. The method according to claim 1, wherein,
in step c) two or more layers of the one or more forming elements are applied overlapping one another and/or the one or more forming elements are applied by means of 3D printing.
8. (canceled)
9. The method according to claim 1, wherein
the register tolerance between the one or more forming elements and the decorative ply lies in a range of from 0.05 mm to 1.0 mm.
10. The method according to claim 1, wherein
the decorative ply has one or more decorative elements, which have been or are applied by means of one or more layers selected from: one or more color layers, one or more reflective layers, one or more optically active and/or optically variable structures.
11. The method according to claim 1, wherein
the method further comprises the following step:
b1) preparing and/or producing a masking area and/or a viewing area in the transfer ply.
12. The method according to claim 11, wherein,
in or after step b1) the viewing area is produced in the transfer ply, and it has a transmittance which is higher than the transmittance of the masking area and/or in a range of from 10% to 100%, and/or wherein the masking area is formed by means of a mask layer.
13. The method according to claim 11, wherein
the viewing area is formed by one or more voids and/or open areas.
14. The method according to claim 11, wherein
the viewing area is arranged congruent with the one or more forming elements at least in partial areas and/or wherein the masking area does not overlap the one or more forming elements.
15. The method according to claim 11, wherein
the one or more forming elements and the viewing area and/or the masking area are arranged register-accurately with respect to one another.
16. The method according to claim 11, wherein
the register tolerance between the one or more forming elements and the viewing area and/or the masking area lies in a range of from 0.05 mm to 1.0 mm.
17. The method according to claim 11, wherein
the register tolerance between decorative ply and the viewing area and/or the masking area lies in a range of from 0.1 mm to 0.4 mm.
18. The method according to claim 1, wherein
the maximum register tolerance between the one or more forming elements and/or the decorative ply and/or the viewing area and/or the masking area, lies in a range of from 0.15 mm to 0.6 mm.
19. (canceled)
20. (canceled)
21. The method according to claim 1, wherein
the carrier ply is provided with a coating or has a coating on at least one of its main surfaces.
22. The method according to claim 1, wherein
the transfer film is or has been provided with a primer layer.
23. The method according to claim 1, wherein
the carrier ply is detachable from the transfer ply.
24. The method according to claim 1, wherein,
in step c) the position in which the one or more forming elements is applied to the carrier ply is set in dependence on the position of one or more registration marks, wherein the one or more registration marks in each case mark the position of one or more layers of the decorative ply, the viewing area, the masking area, and/or the primer in relation to the carrier ply and/or one another.
25. A method for producing a plastic injection-molded article, which is coated with a transfer film, wherein the method comprises the following steps:
x1) preparing a transfer film, wherein the transfer film has a carrier ply and has a transfer ply comprising a decorative ply, wherein the transfer ply has been or is arranged on the carrier ply,
x2) preparing one or more forming elements on the carrier ply, wherein the one or more forming elements have a three-dimensional shape and have been or are applied register-accurately with respect to the decorative ply,
x3) back-injection molding the transfer film with an injection molding compound, wherein, through the action of the injection-molding compound on the transfer film, a molding of the three-dimensional shape of the one or more forming elements is introduced in the transfer ply register-accurately with respect to the decorative ply.
26. The method according to claim 25, wherein,
during the back-injection molding of the transfer film with the injection-molding compound of step x3) a recessed area, is produced in the transfer ply and/or wherein during the back-injection molding of the transfer film with the injection-molding compound of step x3) a raised area is formed in the transfer ply.
27. The method according to claim 26,
the raised area and/or the recessed area has a minimum line width and/or a minimum dot size in a range of from 0.025 mm to less than 0.1 mm.
28. The method according to claim 25, wherein
the following step is carried out before and/or after step x3):
b2) producing a viewing area in the transfer ply, wherein the viewing area is arranged register-accurately with respect to the one or more forming elements, the molding and/or the decorative ply.
29. The method according to claim 25, wherein
during or after the back-injection molding of the transfer film with the injection-molding compound, the plastic injection-molded article is provided with one or more functional component parts.
30. The method according to claim 29, wherein
the one or more functional component parts have at least one of the following components: one or more sensors, one or more illuminants, one or more light-conducting component parts, one or more printed circuit boards and/or combinations thereof.
31. (canceled)
32. (canceled)
33. The method according to claim 29, wherein
the one or more functional component parts, and/or the one or more illuminants, and the one or more forming elements, the molding, the decorative ply, the viewing area and/or the masking area are arranged register-accurately with respect to one another.
34. The method according to claim 25, wherein
the register tolerance between the one or more functional component parts and/or the one or more illuminants, and the one or more forming elements, the molding, the decorative ply, the viewing area and/or the masking area is at most 0.3 mm.
35. The method according to claim 25, wherein
the method further comprises the following step:
flooding the transfer ply and/or the injection-molding compound at least in areas with a polyurethane-containing composition and/or with a polyurea-containing composition.
36. A transfer film having a carrier ply, a transfer ply comprising a decorative ply, wherein the transfer ply is arranged on the carrier ply, and comprising one or more forming elements, wherein the one or more forming elements are applied to the carrier ply and register-accurately with respect to the decorative ply.
37. The transfer film according to claim 36, wherein
the transfer ply is arranged on a first side of the carrier ply and the one or more forming elements are arranged on a second side of the carrier ply lying opposite the first side.
38-43. (canceled)
44. The transfer film according to claim 36, wherein
the one or more forming elements comprises release agents.
45. The transfer film according to claim 36, wherein
the transfer ply has a masking area and/or a viewing area.
46. The transfer film according to claim 45, wherein
the transfer ply has a viewing area which has a transmittance which is higher than the transmittance of the masking area and/or in a range of from 10% to 100%, and/or wherein the masking area is formed by means of a mask layer which reduces the transmittance of the transfer ply in the masking area.
47. The transfer film according to claim 45, wherein
the one or more forming elements and the viewing area and/or the masking area, are arranged register-accurately with respect to one another.
48. The transfer film according to claim 45, wherein
the viewing area is formed by one or more voids and/or open areas.
49. The transfer film according to claim 45, wherein
the viewing area is arranged congruent with the one or more forming elements at least in partial areas and/or wherein the masking area does not overlap the one or more forming elements.
50-54. (canceled)
55. A plastic injection-molded article, comprising an injection-molding compound and a transfer ply of a transfer film, back-injection molded with the injection-molding compound, wherein the transfer ply comprises a decorative ply and has a molding of a three-dimensional shape, wherein the molding is introduced register-accurately with respect to the decorative ply.
56. The plastic injection-molded article according to claim 55, wherein
the molding is formed by means of one or more forming elements.
57. The plastic injection-molded article according to claim 55, wherein
the plastic injection-molded article has a viewing area and/or a masking area register-accurate with respect to the molding and to the decorative ply.
58. The plastic injection-molded article according to claim 57, wherein
the viewing area is formed by one or more voids and/or open areas.
59. The plastic injection-molded article according to claim 55, wherein
the viewing area is arranged congruent with the molding and/or a recessed area of the transfer ply at least in partial areas and/or wherein the masking area does not overlap the molding.
60. The plastic injection-molded article according to claim 58, wherein
the viewing area is arranged congruent with the molding and/or a recessed area of the transfer ply at least in partial areas and/or wherein the masking area does not overlap the molding.
61. The plastic injection-molded article according to claim 55, wherein
the molding is arranged in such a way that the molding does not impair the transillumination properties of the transfer ply.
62. The plastic injection-molded article according to claim 55, wherein
the plastic injection-molded article has one or more functional component parts.
63. The plastic injection-molded article according to claim 62, wherein
the one or more functional component parts, and/or the one or more illuminants, and the one or more forming elements, the molding, the decorative ply, the viewing area and/or the masking area are arranged register-accurately with respect to one another.
64. The plastic injection-molded article according to claim 62, wherein
the register tolerance between the one or more functional component parts and/or the one or more illuminants, and the one or more forming elements, the molding, the decorative ply, the viewing area and/or the masking area is at most 0.3 mm.
发明内容：
[0001]The invention relates to a transfer film, a plastic injection-molded article, and a method for the production thereof.
[0002]It is known to place decorative films in injection molds in IMD methods and to back-injection mold them with a plastic compound. During the back-injection molding, the decorative film adopts a shape complementary to the injection mold. After the back-injection molding, the carrier ply is peeled off the decorative film. It is further known here to introduce surface structures into the surface exposed in this way. However, a change of the shape to be produced requires a change of the injection mold and the surface structures are not arranged register-accurately with respect to the decoration of the decorative film.
[0003]The object of the present invention is thus to specify a transfer film and a plastic injection-molded article coated with a transfer film with improved properties, in particular improved decorative and/or functional properties, as well as improved methods for the production thereof.
[0004]The object is achieved by means of a method for producing a transfer film, in particular IMD transfer film (IMD=In-Mold Decoration). In the method, the following steps are carried out, in particular in the specified order:[0005]a) preparing a carrier ply,[0006]b) preparing a transfer ply comprising a decorative ply, wherein the transfer ply has been or is arranged on the carrier ply,[0007]c) applying one or more forming elements to the carrier ply, wherein the one or more forming elements have a three-dimensional shape and are applied register-accurately with respect to the decorative ply.
[0008]The object is further achieved by means of a transfer film, in particular IMD transfer film. The transfer film is preferably produced by means of the method according to the invention. The transfer film has a carrier ply and a transfer ply comprising a decorative ply, wherein the transfer ply is arranged on the carrier ply. The transfer film further comprises one or more forming elements, wherein the one or more forming elements are applied to the carrier ply and register-accurately with respect to the decorative ply.
[0009]The object is further achieved by means of a method for producing a plastic injection-molded article which is coated with a transfer film, in particular IMD transfer film. Here, the transfer film is preferably produced according to the method according to the invention for producing a transfer film and/or a transfer film according to the invention. The method for producing the plastic injection-molded article comprises the following steps, in particular in the specified order:[0010]x1) preparing a transfer film, wherein the transfer film has a carrier ply, and has a transfer ply comprising a decorative ply, wherein the transfer ply has been or is arranged on the carrier ply,[0011]x2) preparing one or more forming elements on the carrier ply, wherein the one or more forming elements have a three-dimensional shape and have been or are applied register-accurately with respect to the decorative ply,[0012]x3) back-injection molding the transfer film with an injection-molding compound, wherein, through the action of the injection-molding compound on the transfer film, a molding of the three-dimensional shape of the one or more forming elements is introduced into the transfer ply register-accurately with respect to the decorative ply.
[0013]The method for producing the plastic injection-molded article is thus in particular an IMD injection molding method.
[0014]The object is further achieved by a plastic injection-molded article. The plastic injection-molded article is in particular produced using the method according to the invention for producing the plastic injection-molded article. The plastic injection-molded article comprises an injection-molding compound and a transfer ply of a transfer film, in particular IMD transfer film, back-injection molded with the injection-molding compound. The transfer film is in particular produced using the method according to the invention for producing a transfer film and/or a transfer film according to the invention. The transfer ply comprises a decorative ply and has a molding of a three-dimensional shape, wherein the molding is introduced register-accurately with respect to the decorative ply.
[0015]The molding of the three-dimensional shape is thus in particular not merely the shape of a mold half of an injection molding machine. The molding is preferably a molding which is additionally introduced in the shape of the transfer ply which is produced by a mold half against which the carrier ply and/or the one or more forming elements rest during the back-injection molding of the transfer film with the injection-molding compound.
[0016]It is hereby achieved in particular that haptic and/or tactile elements and/or depth effects can be produced on the surface of the plastic injection-molded article. It is further achieved that the haptic and/or tactile elements and/or the depth effects can be produced register-accurately with respect both to decorative elements and/or to backlighting masks and/or to functional component parts, such as e.g. backlights and/or touch sensors of the plastic injection-molded article. It is possible here that the transillumination properties of the plastic injection-molded article are not impaired. It is in particular made possible to prepare haptic and/or tactile elements and/or depth effects on a plastic injection-molded article which, due to their register-accurate arrangement with respect to the decorative ply and optionally to a mask layer and/or to functional component parts, guarantee an improved operation and/or perception during use of the plastic injection-molded article.
[0017]It is further made possible that the need to produce new molds for different surface structures can be reduced and/or shapes prepared by means of a mold can be supplemented by a further three-dimensional shape and in particular individualized. In addition, it is achieved that transfer films and thus coated plastic injection-molded articles can be manufactured cost-effectively in small batch sizes. If shapes prepared by means of a mold are supplemented by means of the three-dimensional shape, the advantage can thus also be achieved that the positioning of the transfer film in the injection molding machine can be configured more efficiently. Depending on the application, for example, a deviation of the relative position between the decorative ply and the mold of the injection molding machine from a target position can be disregarded at least to a certain extent. Since the molding of the three-dimensional shape is always arranged register-accurately with respect to the decorative ply due to the register-accurate application of the one or more forming elements with respect to the decorative ply, a precise impression of the arrangement of the different components of the plastic injection-molded article is retained. Here, all functional component parts can further be arranged register-accurately with respect to the molding of the three-dimensional shape and at the same time with respect to the decorative ply and optionally a mask layer, with the result that the functional component parts can function and be operated precisely.
[0018]Advantageous designs of the invention are described in the dependent claims.
[0019]By registered or register or registration-accurately or register-accurately or registration accuracy or register accuracy is meant a positional accuracy of two or more layers relative to one another. The register accuracy is to range within a predefined tolerance, the register tolerance, which is to be as small as possible. At the same time, the register accuracy of several elements and/or layers relative to one another is an important feature in order to increase the process reliability. The positionally accurate positioning can in particular be effected by means of sensorily, preferably optically, detectable registration marks or register marks. These registration marks or register marks can either represent specific separate elements or areas or layers or themselves be part of the elements or areas or layers to be positioned.
[0020]By a layer and/or a ply is meant in particular a substantially two-dimensional structure which is preferably formed over the whole surface or patterned and itself is preferably single-layered or multi-layered.
[0021]By a haptic element is meant in particular an element which is haptically perceptible. By a tactile element is meant in particular an element which is tactilely perceptible.
[0022]A functional component part is in particular a component part with an electrical, in particular electronic, function. By a functional component part is preferably meant a component part which makes an interaction with a user possible, preferably through information input and/or information output.
[0023]It is possible that during step b) the preparing comprises an application of the transfer ply comprising at least the decorative ply to the carrier ply. The one or more forming elements are preferably applied partially to the carrier ply and/or applied in partial areas with a greater thickness than in other partial areas. An application of layers to the carrier ply can in particular take place directly to the carrier ply or indirectly via one or more further layers.
[0024]Areas, and in particular also partial areas, are preferably specified in the case of a viewing perpendicularly onto a plane and/or main surface spanned by the transfer film or a respective layer, and preferably comprise all parts of the transfer film and/or of the plastic injection-molded article overlapping this plane and/or main surface.
[0025]It is possible that the transfer ply has been or is applied to a first side of the carrier ply and the one or more forming elements have been or are applied to a second side of the carrier ply lying opposite the first side.
[0026]In an advantageous embodiment of the plastic injection-molded article and/or of the method for the production thereof, the molding has been and/or is in particular arranged in such a way that the molding does not impair the transillumination properties of the transfer ply, in particular the decorative ply and/or the mask layer, and/or the injection-molding compound. By not impaired is meant in particular that the molding is arranged in such a way that the molding has substantially no influence on the wavelength, in particular the color, and/or the scattering and/or the lightness and/or the luminance of a radiation being transmitted through a viewing area of the transfer ply, in particular of the light being transmitted through the viewing area of the transfer ply. For example, the transfer ply, in particular the protective layer of the transfer ply, can be transilluminated uniformly in the viewing area, in particular when the transfer ply already has the molding.
[0027]Expediently, the molding does not overlap the viewing area or, if the molding does overlap the viewing area, it is guaranteed that the transfer ply, in particular the protective layer of the transfer ply, has substantially no layer thickness changes in the viewing area. This can be achieved for example when the viewing area is overlapped over the whole surface by the molding.
[0028]It is further possible that the one or more forming elements have a constant layer thickness at least in the viewing area for this purpose.
[0029]In other words, this means that the transillumination properties are not, or not significantly, impaired. By transillumination properties is meant, for example, in particular the light scattering and/or the luminous intensity and/or the light color and/or the wavelength and/or the luminance and/or the radiation angle.
[0030]The back-injection molding of the transfer film with the injection-molding compound preferably takes place at a temperature of the injection-molding compound in a range of from 200° C. to 300° C. The injection-molding compound preferably comprises or in particular consists of ABS, ASA, PA, PP, PC, PMMA, SAN, TPO or a mixture of two or more of the named materials.
[0031]Before the back-injection molding of the transfer film, the transfer film is preferably arranged in an injection molding machine on a mold half, in particular arranged between two mold halves, wherein the mold halves are closed before the back-injection molding. Through the back-injection molding of the transfer film with the injection-molding compound, the transfer film is in particular pressed against a mold half and forms a shape complementary to the mold half. The molding of the plastic injection-molded article has been or is in particular formed by means of the one or more forming elements. It is possible that the one or more forming elements and/or the carrier ply are then removed from the plastic injection-molded article or are removed in the in particular finished plastic injection-molded article.
[0032]By a three-dimensional shape of the forming elements and/or of the molding is meant in particular that the dimensions in all three spatial directions substantially contribute to the design of the one or more forming elements or the molding. Through the three-dimensional shape, in particular at least one surface of the transfer ply has been or is thus curved, in particular in addition to a curvature brought about by a mold half of the injection molding machine.
[0033]The one or more forming elements preferably form one or more motifs or comprise them and/or are introduced into the transfer film in particular for the formation of one or more motifs, in particular the molding in the plastic injection-molded article. It is in particular possible that the outer contours of a projection of the one or more forming elements and/or the molding into a plane follow the outer contours of an in particular two-dimensional motif. It is also possible that the three-dimensional shape comprises a two-dimensional motif and the two-dimensional motif is preferably provided with a three-dimensional structure, for example because the two-dimensional motif is provided with a height in a third spatial direction. The height of the two-dimensional motif is, for example, the thickness or height of a forming element and/or the height of the molding. It is further possible that a three-dimensional shape is a motif which can only be depicted by a three-dimensional structure. A motif is for example selected from or is a combination of figural representation, image, symbol, logo, coat of arms, portrait, pattern, alphanumeric character, in particular 3D lettering, wherein it can preferably be positive and/or negative images. Thus, the motifs can be provided for depth effects and/or haptic and/or tactile elements.
[0034]In particular, during the back-injection molding of the transfer film with the injection-molding compound of step x3), a recessed area is produced in the transfer ply, wherein the recessed area is preferably formed by the molding and in particular contains a positive image of the one or more forming elements. It is also possible that, during the back-injection molding of the transfer film with the injection-molding compound of step x3), a raised area, which in particular contains a negative image of the one or more forming elements, is formed in the transfer ply. It is thus possible that the raised area and/or the recessed area and/or the molding forms one or more motifs, which are in particular complementary to the one or more motifs of the one or more forming elements. A raised area is in particular an area in which there is no forming element present in the transfer film and/or in which the transfer ply deforms in the direction of the carrier ply during the back-injection molding with the injection-molding compound. A recessed area is in particular an area in which a forming element is present in the transfer film and/or in which the transfer ply does not move, or substantially does not move, in the direction of the carrier ply during the back-injection molding with the injection-molding compound. The raised and/or the recessed area can be a continuous area or alternatively or additionally comprise one or more partial areas separate from one another. The transfer ply has been or is preferably arranged at least on a boundary line between an with the one or more forming elements and an area without forming elements, preferably when viewed perpendicularly onto a plane spanned by the transfer film. It is hereby possible that, for example through an action of pressure and/or heat on the transfer film, the transfer ply is deformed register-accurately with respect to the decorative ply, in particular by producing the raised area and the recessed area.
[0035]It is possible that one or more first layers of the one or more forming elements contain or consist of a digital printing ink, preferably contain or consist of an inkjet printing ink, preferably a UV inkjet printing ink. In particular in the method for producing the transfer film in step c), one or more first layers of the one or more forming elements are applied using a digital printing method, preferably an inkjet printing method, preferably a UV inkjet printing method.
[0036]It is further possible that one or more layers of the one or more forming elements are crosslinkable or crosslinked, in particular by means of radiation, preferably UV radiation.
[0037]By means of a digital printing method it is in particular achieved that a small batch size, in particular a batch size of one, can be realized. Further, by means of digital printing methods, in particular UV inkjet printing methods, the register tolerance is improved.
[0038]In the digital printing method, one or more layers are preferably printed by means of one or more printing inks selected from CMYK inks (CMYK=Cyan, Magenta, Yellow, Black) or spot colors, for example white or metallic inks.
[0039]It is furthermore also conceivable that, in particular in step c), one or more layers of the one or more forming elements have been or are applied by means of gravure printing and/or flexographic printing and/or screen printing. It is thus also possible that one or more layers of the one or more forming elements of the transfer film comprise a gravure printing ink and/or a flexographic printing ink and/or a screen printing ink.
[0040]It is in particular possible that the one or more forming elements are single-layered or multi-layered. Preferably, two or more layers of the one or more forming elements are, in step c), and/or have been, in the transfer film, applied overlapping one another and/or the one or more forming elements are applied at least partially by means of 3D printing. It is hereby made possible for example to increase the height of the one or more forming elements starting from the carrier ply. It is further possible that several layers of the one or more forming elements are or have been applied by means of the same printing method and/or several layers are or have been applied by means of different printing methods. By 3D printing can be meant, for example, Selective Laser Sintering (SLS), Fused Deposition Modeling (FDM) and/or stereolithography (SLA).
[0041]It is in particular possible that at least two different printing methods are used for the application of the one or more forming elements. It is for example possible to apply one or more first layers of the one or more forming elements by means of a printing method which is preferably not a digital printing method, for example by means of screen printing. A large, non-individualized surface area of the one or more forming elements is in particular applied using it. It is further possible that at least one layer of the one or more forming elements applied last in step c) is applied using a digital printing method, preferably an inkjet printing method, preferably a UV inkjet printing method. In particular, at least one layer of the one or more forming elements, which forms an outer surface of the transfer film, contains or consists of a digital printing ink, preferably an inkjet printing ink, preferably a UV inkjet printing ink. A spatial separation of applications of different layers can herewith be achieved for example in step c). An individualization, preferably in the form of small surface areas, is hereby made possible for example, in particular before and/or after transport, storage and in particular shortly before and/or at the location of the production of the plastic injection-molded article.
[0042]It is further possible that a molding with various heights is or has been produced in the plastic injection-molded article by means of various heights of the one or more forming elements. This is achieved in particular through the use of suitable settings in the digital printing method, preferably through the number of overlapping printing inks and/or layers of a forming element, the individual ink drop sizes, the UV curing parameters, the application weight of the individual printing inks and/or a combination thereof. It is thus possible that the transfer film contains one or more forming elements of various heights and/or that the plastic injection-molded article contains a molding with various heights and/or depths, in particular contains partial areas of the raised area with various heights and/or partial areas of the recessed area with various heights.
[0043]The layer thickness of a layer of the one or more forming elements applied by means of digital printing preferably lies in a range of from 0.5 μm to 50 μm, in particular in a range of from 1 μm to 25 μm.
[0044]It is further possible that at least one forming element of the one or more forming elements printed by means of digital printing has a layer thickness of from 1 μm to 200 μm. The layer thickness of at least one forming element of the one or more forming elements in particular lies in a range of from 1 μm to 200 μm. Here, several, preferably all, layers of the at least one forming element are preferably applied by means of digital printing and in particular overlapping.
[0045]It is further possible that a layer of the one or more forming elements printed by means of gravure printing has a layer thickness in a range of from 1 μm to 25 μm and/or that a layer of the one or more forming elements printed by means of screen printing has a layer thickness in a range of from 1 μm to 100 μm.
[0046]The height of the molding of the plastic injection-molded article which is achieved in particular in the method for producing the plastic injection-molded article preferably lies in a range of from 1 μm to 200 μm.
[0047]It is further possible that the method contains the following step:[0048]irradiating the one or more forming elements, in particular by means of UV irradiation, wherein one or more irradiation steps are carried out, which are preferably carried out after step c) and/or during step c), in particular before to at least one layer of the one or more forming elements is applied, overlapping, to at least one other layer of the two or more layers of the one or more forming elements.
[0049]The irradiation during step c), in particular before to at least one layer of the one or more forming elements is applied, overlapping, to at least one other layer of the two or more layers of the one or more forming elements, is advantageous because the viscosity of the respectively lower layer is thereby increased, with the result that for one thing this layer does not run and for another subsequent layers obtain a more stable substrate. It is conceivable that overlapping layers are cured in between so that they do not run, for example, and e.g. a higher height-to-width ratio can thereby be achieved.
[0050]The one or more forming elements have been or are preferably formed from the class of the polyacrylates and/or polymethacrylates, polyurethanes, in particular from the group of the polyester polyols, polyether polyols, polycarbonate polyols, polyacrylate polyols and/or combinations of these polymers, polyesters, polyethers, polyolefins, epoxy resins and/or from derivatives of those named. These formulations can in particular be both uncrosslinked and further crosslinked, preferably by isocyanates, carbodiimides, melamines and/or aziridines and/or derivatives of the named compounds.
[0051]The one or more forming elements can further and in particular be built up from radiation-curing acrylates and/or methacrylates, consisting of polyacrylic acrylates, polyurethane acrylates, polyester acrylates, polycarbonate acrylates and/or polyether acrylates and/or copolymers of those named. The radiation-curing formulations, in particular the radiation-curing acrylates and/or methacrylates, are preferably oligomers here. An oligomer is in particular a molecule with a number of monomers in a range of from 2 to 100.
[0052]The one or more forming elements preferably contain, in particular in addition to the named polyacrylates, further UV-curable acrylate monomers and/or methacrylate monomers, and/or are produced therefrom. Depending on the embodiment, these monomers in particular contain one or more acrylate groups and/or preferably further side groups such as e.g. alkyl, aryl, cycloalkyl, cycloalkylaryl, alkoxyalkyl, alkoxyaryl, thionyl, thionylaryl, cyclothionyl, cyclothionylaryl, alkoxythionyl, cycloalkoxythionyl, alkoxycyclothionyl, cycloalkoxycyclothionyl, alkoxythionylaryl, cycloalkoxythionylaryl, alkoxycyclothionylaryl and/or cycloalkoxycyclothionylaryl groups. Special varnish properties, such as e.g. the viscosity and an optimized formation of the three-dimensional network during the radiation curing, can hereby in particular be set. Through the selection of the monomers or combinations of them in particular further properties, such as e.g. the surface hardness or residual tack (usually referred to with the term “tackiness”), of the one or more forming elements can be controlled in a targeted manner.
[0053]The one or more forming elements can, in particular within the meaning of a combination of the above-named, consist of a radiation-curing dual cure varnish. Dual cure varnishes can consist of different polymers or oligomers, which have unsaturated acrylate groups and/or methacrylate groups. These functional groups can in turn be radically crosslinked with one another in the radiation-curing step. For the thermal pre-crosslinking in the first step, at least two or more alcohol groups are preferably also used in the case of these polymers or oligomers. These alcohol groups can in particular be crosslinked with multifunctional isocyanates or melamine formaldehyde resins. Various UV raw materials such as epoxy acrylates, polyether acrylates, polyester acrylates and in particular polyacrylic acrylates come into consideration for example as preferably unsaturated oligomers or polymers. In particular blocked and/or unblocked representatives based on TDI (TDI=toluene-2,4-diisocyanate), HDI (HDI=hexamethylene diisocyanate) or IPDI (IPDI=isophorone diisocyanate) are used as isocyanate. The melamine crosslinkers can come from the group of the fully etherified, the imino types and/or the benzoguanamines.
[0054]In a preferred embodiment, the one or more forming elements have been or are built up as a color layer, e.g. for better legibility in the later positioning and in particular for the register-accurate application of later-applied components. Here, the color layer can consist of or comprise colorants and/or pigments, in particular also optically variable pigments and/or metallic pigments. The one or more forming elements can in particular, for the optimization of rheological properties, also have been or be equipped with fillers such as for example HDK (fine-particle silica).
[0055]The one or more forming elements have been or are provided with release agents, in particular for improving the properties of detachment from an injection mold, in particular from the mold half which is in contact with the one or more forming elements in step x3). The release agents are preferably silicones. In particular for better integration in the three-dimensional network of the one or more forming elements, these silicones can for their part be equipped with side chains, which bear radiation-curable groups. These groups have been or are preferably formed from the classes of radiation-curing acrylates and/or methacrylates, consisting of and/or comprising acrylic acrylates, urethane acrylates, ester acrylates, carbonate acrylates and/or ether acrylates and/or copolymers of those named. Each of these groups, as well as the silicone itself, can in turn in particular bear terminal groups, which preferably contribute to the thermal crosslinking in the one or more forming elements. These terminal groups can in particular be alcohol groups, multifunctional isocyanates or melamine formaldehyde resins. Both blocked and unblocked representatives based on TDI (TDI=toluene-2,4-diisocyanate), HDI (HDI=hexamethylene diisocyanate) or IPDI (IPDI=isophorone diisocyanate) are preferably used as isocyanate. The melamine crosslinkers are in particular selected from the group of the fully etherified, the imino types and/or the benzoguanamines. The silicones can furthermore bear side groups, which in particular do not contribute to the crosslinking but nevertheless influence the properties of the relevant silicone in a targeted manner. These side groups can be selected e.g. from one or more of the substance classes of the alkyl, aryl, cycloalkyl, cycloalkylaryl, alkoxyalkyl, alkoxyaryl, thionyl, thionylaryl, cyclothionyl, cyclothionylaryl, alkoxythionyl, cycloalkoxythionyl, alkoxycyclothionyl, cycloalkoxycyclothionyl, alkoxythionylaryl, cycloalkoxythionylaryl, alkoxycyclothionylaryl or cycloalkoxycyclothionylaryl groups.
[0056]The one or more forming elements preferably contain so-called UV initiators, in particular for the initiation of the radiation curing, if this is in particular a UV-radiation curing. The UV initiators are preferably selected from the class of the α-alkoxy, α-hydroxy or α-amino-aryl ketones and/or the class of the acyl phosphine oxides. Acyl phosphine oxides are preferably used in combination with UV inkjet printing of the one or more forming elements in particular because of their particularly suitable absorption properties in the UV-LED range.
[0057]In particular for the improvement of special and typical varnish properties, such as e.g. the wetting, the running, the foam formation etc., it is possible that the one or more forming elements contain additives. For integrating these additives in the three-dimensional network, they are typically provided for their part with radiation-curing or thermally crosslinkable groups or combinations thereof.
[0058]In particular for the minimization of chain terminations during the radiation curing through reactions of the formed radicals with oxygen molecules from the air and/or for the reduction of the migration of radical chains on the forming element surface, tertiary amines and/or acrylate amines, in particular so-called amine synergists, are preferably added to the one or more forming elements. In particular for integrating these additives in the three-dimensional network, they are preferably likewise provided for their part with radiation-curing or thermally crosslinkable groups or combinations thereof.
[0059]It is possible that the raised area and/or the recessed area has a minimum line width and/or a minimum dot size in a range of from 0.025 mm to 0.1 mm. By the minimum line width is meant in particular the minimum width of an area. The minimum dot size is in particular the minimum diameter of an area with a circular footprint.
[0060]It is further possible that the recessed area has a minimum line width and/or minimum dot size of more than 0.025 mm, preferably for the production of a positive image of the one or more forming elements, in particular for the case where the one or more forming elements have been or are applied by means of digital printing.
[0061]It is further possible that the raised area has a minimum line width and/or minimum dot size of more than 0.040 mm, preferably for the production of a negative image of the one or more forming elements, in particular for the case where the one or more forming elements have been or are applied by means of digital printing.
[0062]It is further possible that the recessed area has a minimum line width and/or minimum dot size of more than 0.075 mm, preferably for the production of a
具体实施方式：
[0160]FIG. 1 shows, schematically, a method for producing a transfer film. The transfer film is in particular an IMD transfer film. Here, the following steps are carried out, in particular in the specified order:[0161]a) preparing 101 a carrier ply,[0162]b) preparing 102 a transfer ply comprising a decorative ply, wherein the transfer ply has been or is arranged on the carrier ply,[0163]c) applying 103 one or more forming elements to the carrier ply, wherein the one or more forming elements have a three-dimensional shape and are applied register-accurately with respect to the decorative ply.
[0164]FIG. 2 shows, schematically, a method for producing a plastic injection-molded article which is coated with a transfer film. The transfer film is in particular an IMD transfer film. It is possible here that the transfer film is a transfer film as described for the other figures and/or is produced with a method described for them. The method for producing the plastic injection-molded article comprises at least the following steps, in particular in the specified order:[0165]x1) preparing 201 a transfer film, wherein the transfer film has a carrier ply, and has a transfer ply comprising a decorative ply, wherein the transfer ply has been or is arranged on the carrier ply,[0166]x2) preparing 202 one or more forming elements on the carrier ply, wherein the one or more forming elements have a molding and have been or are applied register-accurately with respect to the decorative ply,[0167]x3) back-injection molding 203 the transfer film with an injection-molding compound, wherein, through the action of the injection-molding compound on the transfer film, a molding of the three-dimensional shape of the one or more forming elements is introduced into the transfer ply register-accurately with respect to the decorative ply.
[0168]FIG. 3a shows, schematically, a transfer film 1. The transfer film 1 is in particular an IMD transfer film. The transfer film 1 is preferably produced as is described for example in relation to FIG. 1. The transfer film 1 has a carrier ply 3 and a transfer ply 2. The transfer ply 2 comprises a decorative ply 21 and is arranged on the carrier ply 3. The transfer film 1 further comprises a forming element 40, wherein the forming element 40 is applied to the carrier ply 2 and register-accurately with respect to the decorative ply 21. It is also possible that several forming elements 40 are arranged on the carrier ply 3.
[0169]During the back-injection molding 203 of the transfer film 1 with the injection-molding compound, the one or more forming elements 40 in particular rest against a mold half of the injection molding machine. The injection-molding compound can adhere to the transfer film 1, in particular to the exposed side of a primer, on the side of the transfer film 1 lying opposite the one or more forming elements 40. After the back-injection molding 203, a plastic injection-molded article 10 as shown by way of example in FIG. 3b or FIG. 3c can be obtained.
[0170]FIG. 3b shows, schematically, a plastic injection-molded article 10. The plastic injection-molded article 10 is, for example, produced as is described in relation to one of FIGS. 1, 2 and 3a. The plastic injection-molded article 10 comprises an injection-molding compound 5 and a transfer ply 2 of a transfer film 1 back-injection molded with the injection-molding compound 5. The transfer film 1 is in particular an IMD transfer film, preferably as is described in relation to FIG. 1 and/or FIG. 3a and/or produced as is described in relation to FIG. 1 and/or FIG. 3a. The transfer ply 1 comprises a decorative ply 21 and has a molding 41 of a three-dimensional shape. Here, the molding 41 is introduced register-accurately with respect to the decorative ply 21.
[0171]A viewing of areas, such as for example the areas 71, 72, 81 and 82, takes place in particular onto a main surface spanned by a respective layer or the transfer film 1, in FIG. 3 preferably from right to left or vice versa. Preferably when viewed perpendicularly onto a plane and/or main surface spanned by the transfer film 1 or a respective layer, areas, and in particular also partial areas, preferably comprise all parts of the transfer film 1 and/or of the plastic injection-molded article 10 overlapping this plane and/or main surface.
[0172]The molding 41 of the plastic injection-molded article has been or is in particular formed by means of the one or more forming elements 40. Thus, the molding 41 in particular forms a shape complementary to the three-dimensional shape of the one or more forming elements 40. As is shown by way of example in FIG. 3b and FIG. 3c, the one or more forming elements 40 can preferably be removed from the plastic injection-molded article 10 in particular together with the carrier ply 3. It is also conceivable that at least the carrier ply 3 and optionally the one or more forming elements 40 and/or residues thereof still adhere to the plastic injection-molded article 10. A protection of the surface of the plastic injection-molded article 10 can herewith be guaranteed in particular, e.g. during transport and/or storage.
[0173]In the areas in which no forming elements are arranged, the carrier ply 3 is pressed against the mold half at least in areas during the back-injection molding 203 of the transfer film with the injection-molding compound 5 of step x3) and the molding 41 of the one or more forming elements 40 in the transfer ply 21 is thereby formed, wherein here the molding 41 in particular makes the haptics and/or the depth effect possible.
[0174]The one or more forming elements 40 have, here in particular in comparison with the carrier ply 3 and the transfer ply 2, a three-dimensional shape because in particular both the height of the forming element 40 and the dimensions in the other spatial directions contribute significantly to the design of the forming element 40, which is the case in particular since the height of the molding 41 of the plastic injection-molded article 10 herewith turns out to be dependent on the design of the forming element 40. The three-dimensional shape for example comprises a two-dimensional motif and the two-dimensional motif has been or is preferably provided with a spatial structure, for example by increasing the thickness or height of the two-dimensional motif, here along the horizontal, in particular in a targeted manner.
[0175]The carrier ply 3 is preferably a PET carrier ply. With respect to further possible materials and an optional coating of the carrier ply 3, reference is made in particular to the above statements. The carrier ply 3 for example has a layer thickness of 75 μm, which is the case in particular for use in the automotive sector. It is also possible that the carrier ply 3 has a layer thickness of 50 μm, for example for the production of laptop sleeves. It is in particular possible that the carrier ply 3 has a degree of elongation at break in a range of from 110% to 135%. The degree of elongation is in particular the quotient of the length of the carrier ply in the direction of an elongation in relation to the corresponding length of the carrier ply in the unstretched state. By the degree of elongation is in particular also meant an average stretchability. For example, the carrier ply in particular has an average stretchability of 25%. Here, the direction of the average stretchability is in particular based on an X direction and/or a Y direction. Here, the X direction, for example in FIG. 3a, preferably points along a horizontal and/or the Y direction, for example in FIG. 3a, points along a vertical. It is further possible that the carrier ply has a tensile strength in a range of from 15 kpsi to 50 kpsi, preferably in a range of from 27 kpsi to 31 kpsi and/or a modulus of elasticity in a range of from 100 kpsi to 1000 kpsi, preferably in a range of from 300 kpsi to 700 kpsi.
[0176]It is further possible that during step b) the preparing comprises an application of the transfer ply comprising at least the decorative ply 21 to the carrier ply 3. The one or more forming elements 40 are preferably partially applied to the carrier ply 3. It is also possible that the one or more forming elements 40 have been or are applied in partial areas with a greater thickness than in other partial areas. An application of the one or more forming elements 40 to the carrier ply 3 can in particular take place directly to the carrier ply 3 or indirectly via one or more further layers. A height or thickness, for example in FIG. 3b, is in particular measured along a horizontal line.
[0177]The transfer ply 2 is preferably first applied to the carrier ply 3 and then in particular the one or more forming elements 40 are applied to the carrier ply 3 register-accurately at least with respect to the decorative ply 21, in particular to the side of the carrier ply 3 lying opposite the transfer ply 2.
[0178]One or more first layers of the one or more forming elements 40 in particular contain or consist of a digital printing ink. The digital printing ink is preferably an inkjet printing ink, preferably a UV inkjet printing ink. In particular, in the method for producing the transfer film 1, in step c) one or more first layers of the one or more forming elements 40 are applied using a digital printing method, preferably an inkjet printing method, preferably a UV inkjet printing method. It is further possible that one or more layers of the one or more forming elements are crosslinkable or crosslinked, in particular by means of radiation, preferably UV radiation. By means of a digital printing method it is in particular achieved that a small batch size, in particular a batch size of one, can be realized. Further, the register tolerance is improved by means of digital printing methods, in particular UV inkjet printing methods. In the digital printing method, one or more layers are preferably printed by means of one or more printing inks selected from CMYK inks (CMYK=Cyan, Magenta, Yellow, Black).
[0179]It is furthermore also conceivable that, in particular in step c), one or more layers of the one or more forming elements 40 have been or are applied by means of gravure printing and/or screen printing. It is thus also possible that one or more layers of the one or more forming elements 40 of the transfer film comprise a gravure printing ink and/or a screen printing ink.
[0180]It is in particular possible that the one or more forming elements 40 are single-layered or multi-layered. In step c) and/or in the transfer film 1, two or more layers of the one or more forming elements 40 are preferably applied overlapping one another and/or the one or more forming elements 40 are applied at least partially by means of 3D printing. It is hereby made possible for example to increase the height of the one or more forming elements 40 starting from the carrier ply 3. It is further possible that several layers of the one or more forming elements 40 are or have been applied by means of the same printing method and/or several layers are or have been applied by means of different printing methods.
[0181]It is in particular possible that at least two different printing methods are used for the application of the one or more forming elements 40. It is for example possible to apply one or more first layers of the one or more forming elements 40 by means of a printing method which is preferably not a digital printing method, for example by means of screen printing. A large, non-individualized surface area of the one or more forming elements is in particular applied using it. It is further possible that at least one layer of the one or more forming elements 40 applied last in step c) is applied using a digital printing method, preferably an inkjet printing method, preferably a UV inkjet printing method. In particular, at least one layer of the one or more forming elements 40, which forms an outer surface of the transfer film 1, contains or consists of a digital printing ink, preferably an inkjet printing ink, preferably a UV inkjet printing ink. A spatial separation of applications of different layers can herewith be achieved for example in step c). An individualization, preferably in the form of small surface areas, is hereby made possible for example, in particular before and/or after transport, storage and in particular shortly before and/or at the location of the production of the plastic injection-molded article 10.
[0182]It is further possible that a molding 41 with various heights is or has been produced in the plastic injection-molded article 10 by means of various heights of the one or more forming elements 40. This is achieved in particular through the use of suitable settings in the digital printing method, preferably through the number of overlapping printing inks and/or layers of a forming element, the individual ink drop sizes, the UV curing parameters, the application weight of the individual printing inks and/or a combination thereof. It is thus possible that the transfer film 1 contains one or more forming elements 40 of various heights and/or that the plastic injection-molded article 10 contains a molding 41 with various heights and/or depths, in particular contains partial areas of the raised area 82 with various heights and/or partial areas of the recessed area 81 with various heights.
[0183]The layer thickness of a layer of the one or more forming elements 40 applied by means of digital printing preferably lies a range of from 0.5 μm to 50 μm, in particular in a range of from 1 μm to 25 μm.
[0184]It is further possible that at least one forming element of the one or more forming elements 40 printed by means of digital printing has a layer thickness of from 1 μm to 200 μm. The layer thickness of at least one forming element of the one or more forming elements 40 in particular lies in a range of from 1 μm to 200 μm. Here, several, preferably all, layers of the at least one forming element are preferably applied by means of digital printing and in particular overlapping.
[0185]It is further possible that a layer of the one or more forming elements 40 printed by means of gravure printing has a layer thickness in a range of from 1 μm to 25 μm and/or that a layer of the one or more forming elements 40 printed by means of screen printing has a layer thickness in a range of from 1 μm to 100 μm.
[0186]It is further possible that the method contains the following step:[0187]irradiating the one or more forming elements 40, in particular by means of UV irradiation, wherein one or more irradiation steps are carried out, which are preferably carried out after step c) and/or during step c), in particular before to at least one layer of the one or more forming elements is applied, overlapping, to at least one other layer of the two or more layers of the one or more forming elements. It is conceivable that overlapping layers are cured in between so that they do not run, for example, and e.g. a higher height-to-width ratio can thereby be achieved.
[0188]With respect to the composition of the one or more forming elements 40, reference is made in particular to the above statements.
[0189]In particular, during the back-injection molding of the transfer film 1 with the injection-molding compound 5 of step x3), a recessed area 81 is produced in the transfer ply 2, wherein the recessed area 81 is preferably formed by the molding 41. The recessed area 81 thus in particular contains a positive image of the one or more forming elements 40. It is further possible that, during the back-injection molding of the transfer film 1 with the injection-molding compound 5 of step x3), a raised area 82 is formed in the transfer ply 2. The raised area 82 thus in particular contains a negative image of the one or more forming elements 40. The raised area 82 and/or the recessed area 81 can be a continuous area or alternatively or additionally comprise one or more partial areas separate from one another. It is thus possible that the raised area 82, the recessed area 81 and/or the molding 41 form one or more motifs, which are in particular complementary to the one or more motifs of the one or more forming elements 40. The raised area 82 is in particular arranged where there is no forming element 40 present in the transfer film 1 and/or in which the transfer ply 3 deforms in the direction of the carrier ply 3 during the back-injection molding with the injection-molding compound 5. The recessed area 81 is in particular arranged where the one or more forming elements 40 are present in the transfer film 1 and/or in which the transfer ply 2 does not move, or substantially does not move, in the direction of the carrier ply 3 during the back-injection molding with the injection-molding compound 5.
[0190]It is possible that the raised area 82 and/or the recessed area 81 has a minimum line width and/or a minimum dot size in a range of from 0.025 mm to 0.1 mm, in particular when the one or more forming elements 40 have been or are applied by means of UV digital printing. By way of example, for the case where the recessed area 81 has a circular footprint and the sectional plane lies in the center thereof, in FIGS. 3b and 3c the dot size would be the distance from the upper to the lower dashed marking of the area 81. By way of example, for the case where the recessed area 81 is a line, which in FIGS. 3b and 3c spreads out in the viewing direction, the line width would preferably be the distance from the upper to the lower dashed marking of the area 81 of the sectional plane shown.
[0191]It is possible in particular that the recessed area 81 has a minimum line width and/or a minimum dot size of more than 0.025 mm and/or the raised area 82 has a minimum line width and/or a minimum dot size of more than 0.040 mm, in particular for the case where the one or more forming elements 40 have been or are applied by means of digital printing. It is also possible that the recessed area 81 has a minimum line width and/or a minimum dot size of more than 0.075 mm and/or the raised area 82 has a minimum line width and/or a minimum dot size of more than 0.12 mm, in particular for the case where the one or more forming elements 40 have been or are applied by means of gravure printing. It is further possible that the recessed area 81 has a minimum line width and/or a minimum dot size of more than 0.10 mm and/or the raised area 82 has a minimum line width and/or a minimum dot size of more than 0.15 mm, in particular for the case where the one or more forming elements 40 have been or are applied by means of screen printing.
[0192]For example, in the case of a produced haptic surface area of approximately 0.5 cm×0.01 cm, no tangible difference, and/or no difference that can be felt by the fingertips, between positive and negative forming element 40 can thus be ascertained. By a positive forming element 40 is meant an isolated forming element 40 which produces a recessed area 81 in the carrier ply 3 after the back-injection molding, when the cross section is viewed. Such a positive forming element 40 is represented in FIGS. 10a and 10b. Wherein FIG. 10a shows the positive forming element 40 before the back-injection molding and FIG. 10b shows the positive forming element 40 after the back-injection molding. By a negative forming element 40 is meant one or more whole-surface forming elements which produce a raised area 82 of the carrier ply 3 after the back-injection molding, when the cross section is viewed. Such a negative forming element 40 is represented in FIGS. 11a and 11b. Wherein FIG. 11a shows the negative forming element before the back-injection molding and FIG. 11b shows the negative forming element after the back-injection molding. As represented in FIGS. 10b and 11b, after the back-injection molding the forming element 40 is preferably flush or almost flush with the surface of the carrier ply, with the result that no tangible difference, and/or no difference that can be felt by the fingertips, between positive and negative forming element 40 can be ascertained.
[0193]In particular, the one or more forming elements 40 have a higher dimensional stability than the carrier ply 3 and/or the transfer ply 2, preferably than at least one layer of the transfer ply 2. By a higher dimensional stability is meant in particular a higher resistance to deformation during the back-injection molding 203 of the transfer film 1 with the injection-molding compound 5.
[0194]The one or more forming elements 40 are preferably mechanically stable and/or have a mechanical stability, in particular in the case of a back-injection molding with the injection-molding compound 5, preferably in an IMD injection-molding process, thus in particular in step x3). By the mechanical stability is meant here in particular the stability of the one or more forming elements 40 with respect to the load acting through the injection-molding compound 5, in particular during the back-injection molding 203 of the transfer film 1 with the injection-molding compound 5. In other words, the one or more forming elements 40 are preferably sufficiently hard and produce a sufficiently strong connection to the carrier film 3, in order to withstand in particular the high pressure which is generated during the back-injection molding 203. For this purpose, the one or more forming elements 40 preferably have a glass transition temperature of more than 200° C. It is further possible that the one or more forming elements 40 have a substantially constant compressive strength up to a temperature of 200° C. In particular the deformation of the transfer ply 3 when the transfer film 1 is exposed to pressure and/or heat, in particular during the back-injection molding of the transfer film 1 with the injection-molding compound, is hereby guaranteed and in particular a high edge-sharpness of the molding 41 is made possible.
[0195]It is possible that the mechanical stability is determined with reference to the difference in height when comparing the height of the one or more forming elements 40 before and after the back-injection molding 203 of the transfer film 1 with the injection-molding compound 5, wherein the height of the one or more forming elements 40 after the back-injection molding 203 of the transfer film 1 with the injection-molding compound 5 corresponds to the height of the molding 41 of the plastic injection-molded article 10.
[0196]The molding 41 preferably has a height in a range of from 90% to 100% of the height of the one or more forming elements 40 of the transfer film 1 before the back-injection molding 203 with the injection-molding compound 5. It is possible that the temperatures arising in the injection mold during the back-injection molding, in particular the temperature of the injection-molding compound, lie or lies in a range of from 150° C. to 500° C., in particular in a range of from 200° C. to 300° C. It is possible that the pressures arising in the injection mold during the back-injection molding, in particular the internal pressure of the injection mold, lie or lies in a range of from 300 bar to 1000 bar, in particular in a range of from 400 bar to 800 bar.
[0197]It is possible for example that the molding 41 after the back-injection molding 203 of the injection-molding compound 5 has a height of 90% of the height of the one or more forming elements 40 before the back-injection molding 203 of the injection-molding compound 5, in particular for the case where the carrier ply 3 has a layer thickness of 50 μm and preferably consists of PET. It is also possible that the molding 41 after the back-injection molding of the injection-molding compound has a height of 100% of the height of the one or more forming elements 40 before the back-injection molding of the transfer film 1 with the injection-molding compound 5, in particular for the case where the carrier ply 3 has a layer thickness of 75 μm and preferably consists of PET. In particular in the case of a layer thickness of the carrier ply 3, which preferably consists of PET, of at least 75 μm the height of the one or more forming elements 40 is maintained or is just as high before the back-injection molding 203 of the transfer film 1 with the injection-molding compound 5 as after the back-injection molding.
[0198]The height of the molding 41 is preferably determined on the plastic injection-molded article 10 in particular with reference to the difference in height between an outer surface of the transfer ply 2 in the recessed area 81 and a neighboring outer surface of the transfer ply 2 in a raised area 82. The height of the one or more forming elements 40 is in particular measured before the back-injection molding 203 of the transfer film 1. The measurement of the height of the molding 41 and/or of the one or more forming elements 40 and/or the line width and/or the dot size is in particular carried out by means of scanning electron microscope (SEM).
[0199]The height of the molding 41 of the plastic injection-molded article 10 which is achieved in particular in the method for producing the plastic injection-molded article 10 preferably lies in a range of from 1 μm to 200 μm.
[0200]Preferably, the one or more forming elements 40 have been, in the transfer film 1, or are, in step c), arranged register-accurately with respect to the decorative ply 21 in at least two different directions. In FIGS. 3a, 3b and 3c, one direction points, for example, along the viewing direction and the other along a vertical line. It is hereby possible for example, in the method for producing the transfer film 1, to apply the one or more forming elements 40 register-accurately with respect to the decorative ply 21 both in the running direction of the carrier ply 3 and transverse to the running direction of the carrier ply 3, in particular to apply them register-accurately with respect to decorative elements separate from one another, for example separate motifs, of the decorative ply 21. It is in particular possible that at least one forming element of the one or more forming elements 40 has been or is arranged register-accurately in each case with respect to at least one decorative element of one or more decorative elements, wherein the at least one decorative element preferably forms a separate motif. A separate motif is in particular not an endless motif and/or has visible boundary lines in the transfer film 1 and/or the plastic injection-molded article 10 in the two different directions. Thus, it is further possible that the molding 41 or at least a partial area of the molding 41 has been or is arranged register-accurately with respect to at least one decorative element of one or more decorative elements.
[0201]The register tolerance between the one or more forming elements 40 and the decorative ply preferably lies in a range of from 0.05 mm to 1.0 mm, preferably in a range of from 0.05 mm to 0.2 mm. The register tolerance between the one or more forming elements 40 and the decorative ply 21 is in particular at most 1.0 mm, preferably at most 0.2 mm. It is thus also possible that the register tolerance between the molding 41 and the decorative ply 21 preferably lies in a range of from 0.05 mm to 1.0 mm, preferably in a range of from 0.05 mm to 0.2 mm, and/or is at most 1.0 mm, preferably at most 0.2 mm.
[0202]A register tolerance in the range of from 0.05 mm to 0.2 mm is in particular achieved when the one or more forming elements 40 are applied by means of a digital printing method, preferably by means of inkjet printing, preferably UV inkjet printing. If the one or more forming elements 40 are applied by means of screen printing, a register tolerance in the range of from 0.2 mm to 1.0 mm is in particular possible.
[0203]FIG. 3c shows the plastic injection-molded article 10 shown in FIG. 3b except that the plastic injection-molded article 10 further has a functional component part 6. The functional component part 6 is preferably arranged register-accurately with respect to the molding 61 and register-accurately with respect to the decorative ply 21.
[0204]It is further possible that the transfer film 1 and/or the plastic injection-molded article 10 has a viewing area 71 and/or a masking area 72. The viewing area 71 is in particular provided so that, in the plastic injection-molded article 10 on the side of the injection-molding compound 5 lying opposite the transfer ply 2, further components can be arranged visible at least at times through the transfer ply 2. The masking area 72 is in particular provided so that the further components arranged in the plastic injection-molded article 10 on the side of the injection-molding compound 5 lying opposite the transfer ply 2 are concealed from view through the transfer ply 2 in the masking area. For this, the method preferably comprises the following step, in particular before and/or after step c):[0205]b1) preparing and/or producing a masking area 72 and/or a viewing area 71 in the transfer ply 3.
[0206]The viewing area 71 preferably has a transmittance which is higher in particular than the transmittance of the masking area 72, is preferably higher than the transmittance of the masking area by a value of at least 10% and/or in a range of from 10% to 100%. The viewing area 71 preferably has a transmittance of more than 50%, in particular more than 75%. The masking area preferably has a transmittance of less than 50%, in particular less than 20%, preferably less than 5%. The transmittance relates in particular to electromagnetic waves, preferably with wavelengths visible to the human eye. In the viewing area, the transfer ply 3 is preferably transparent for light which is visible to the human eye. In the masking area 72, the transfer ply 3 is in particular opaque for light which is visible to the human eye.
[0207]It is also possible that the viewing area 71 is produced in the transfer ply 3, in particular in a mask layer, in or after step b1).
[0208]As is shown by way of example in FIG. 3c, the plastic injection-molded article 10 has been provided in particular with one or more functional component parts 6 and/or is provided with one or more functional component parts 6 during or after the back-injection molding 203 of the transfer film 1 with the injection-molding compound 5. Here, the one or more functional component parts 6 have been or are in particular arranged on the side of the injection-molding compound 5 lying opposite the transfer ply 2. The one or more functional component parts preferably have at least one of the following components: one or more sensors, in particular one or more touch sensors, one or more illuminants, in particular one or more displays, one or more LEDs, one or more light-conducting component parts, one or more printed circuit boards and/or combinations thereof.
[0209]By means of the one or more illuminants, a backlighting is integrated into the plastic injection-molded article 10, for example. It is possible that a backlighting is prepared as a separate component part comprising one or more LEDs on a printed circuit board for this purpose, wherein the one or more LEDs are preferably connected to the printed circuit board via a soldered connection. The one or more illuminants, in particular in the form of LEDs, preferably the backlighting, preferably have been or are arranged in a particularly register-accurate overlapping with the viewing area 71, preferably directly behind and/or in the viewing area 71. It is further possible that the plastic injection-molded article 10 contains one or more diffuser layers and/or one or more light-guide layers. The one or more illuminants, in particular in the form of LEDs, preferably in the form of the backlighting, preferably are or have been integrated into the plastic injection-molded article by means of gluing, screwing, ultrasonic welding, soldering, clamping, heat staking, infrared welding . . . .
[0210]The one or more illuminants, preferably one or more LEDs, have been, in the plastic injection-molded article 10, or are, in particular before the back-injection molding 203 of the transfer film 1 in step x3), arranged preferably on the side of the transfer ply 2 facing away from the carrier ply 3 and/or are connected to the transfer ply 2 during the back-injection molding 203 and optionally to the transfer ply 2 via the injection-molding compound 5. It is further possible that the one or more illuminants, preferably the one or more LEDs, are or have been introduced into the plastic injection-molded article, in particular after the back-injection molding with the